High Alumino Silicate Glass Panel for Cellphone Tablet for Front Touch Screen
High Alumino-Silicate Glass (CHIYAN-H1) is an eco-friendly high aluminosilicate ultra-thin glass, which increases the Al₂O₃ content in the composition to improve the ion exchange efficiency, so that it has excellent mechanical properties after chemical strengthening.
Features:
High Impact Resistance
High Scratch Resistance
High Transmittance
High chemical resistance
High Flexibility
High Bending Strength Resistance
Ultra Clear White
Application: Widely used in high-end consumer electronics device cover, vehicle display, industrial touch panels, smart home screen display etc fields;
Regular Thickness:
0.3mm~6mm
CHIYAN-H1’s 0.3~6.0mm thickness high alumino-silicate glass has already been used in the market to meet a wide range of customers needs.
Standard Size:1300*1100mm (5th Generation)
Note: The size can be customized according to customer's needs.
Product Composition
High Alumino-Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.
Physical Property Parameter
S/N | Items | Unit | CY-M2 |
1 | Density | g/cm3 | 2.47 |
2 | Refractive Index(590nm) | / | 1.51 |
3 | Young's Modulus | Gpa | 75.6 |
4 | Shear Modulus | Gpa | 30.7 |
5 | Volume Resistivity | lg(Ω .cm) | 9.1 |
6 | Dielectric Constant | F/m | 8.2 |
7 | Softening Point | ℃ | 830 |
8 | Strain Point | ℃ | 558 |
9 | Annealing Point | ℃ | 606 |
10 | Transmittance(0.7mmt,550nm) | % | ≥92 |
11 | Thermal Expansivity | * 10-7/℃ | 98 |
12 | Photoelastic Coefficient | nm/cm/MPa | 27.2 |
13 | Poisson's Coefficient | / | 0.23 |
14 | Vickers-hardness | HV | 700 |
Chemical Tempering Process Parameter
CS | >900Mpa |
DOL | >50um |
4PB | >800Mpa |
Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.
Packaging Diagram
Storage
Storage conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.
High Alumino-Silicate Glass(CHIYAN-H1) is adopted Float Glass Process.
Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed: